16mmTracking Duct Rodder Tool FRP Fiberglass Snake Duct Rodder
High Density polyethylene (Grade: for the insulating and jacketing of Telecommunication Cables) is used in the outer diameter coating. Duct Rodders will equipped with different size reel according to the length of rod. There are wheels on the reel, which make it convenient for moving.Light weight, durable, resistance to acid, alkali, aging resistant, corrosion resistant.High tensile strength and bending properties, which make it to go through narrow pipes easily.Good temperature adaptability, the product will not soften in hot weather / nor become brittle in cold weather. Its usability will not be affected by temperature.
Outer protect layer are made of high density polyethylene engineering plastic, which has good anti-UV capability. Cover was coated with long-term UV-resistant polyethylene.
Its surface has the advantage of smooth, wear-resistant and long service life.
Fiberglass Duct Rodder Structure
Constructed of fiberglass reinforced in the center and consists of a rugged plastic layer that would ensure the lifetime of the flexible rod.
Assembly: metal frame and rubber wheels, Wheel assembly for easy transportation; Guide rollers and the right parts for rotary coupling; parking brake for the flexible rod. There is copper wire inside for tracing easily.
Polyethylene cover: Medium density polyethylene resin for the insulating and jacketing of cables.
About the 16mm fiber optic wire puller fish tape cable pulling rotan cable duct rodder We have many size for your choice such as Rod diameter: 4mm;4.5mm;6mm;7mm;8mm;9mm;10mm;11mm;12mm;13mm;14mm;15mm; 16mm ;17mm;18mm; Rod length:50-500m
| | |
| | Epoxy fiber glass(inner core)and inported ABS(out layer) |
Parameter Frame dimension 1300mm*450mm*1330mm, 1200mm*420mm*1220mm, 980mm*350mm*1000mm, 680mm*240mm*700mm, 420mm*180mm*400mm, | Reinforcement | E-Glass Fiber |
| Glass content of inner part | E-Glass Fiber |
| Density | >1.9g/m³ |
| Diameter tolerance | ±0.10mm |
| work situation temperature | -40ºC~+80ºC |
| Min pulling strength | 4000N±5% |
| Tensile modulus | >3000MPa |
| Consistency of rod | 150g±5% |
| Flexural modulus | >3000MPa |
| Elongation at Break | 2.5-3% |